苏州洪大塑胶有限公司

BayblendFR3010
PC/ABS
锑免费，无溴，氯，阻燃

注塑级，提高耐热性，维卡/乙120温度=110°C UL认证94V-0（1.5毫米）锑，氯和溴阻燃灼热丝试验（GWFI）：960℃（2.0毫米），改进的耐化学性和应力开裂行为继任者FR2010

[DatasheetBayblendFR3010HF]

PropertyTestConditionUnitStandardtypicalValueRheologicalproperties Spiralflowlength260°C/80°C2x8mmmmBayertest400Meltvolume-flowrate240°C5kgcm³/10minISO113325 Moldingshrinkage，parallel150x105x3mm240°C/MT80°C%b.o.ISO25770.5-0.7 Moldingshrinkage，normal150x105x3mm240°C/MT80°C%b.o.ISO25770.5-0.7Mechanicalproperties(23°C/50%r.h.)Tensilemodulus1mm/minMPaISO527-1，-22700Yieldstress50mm/minMPaISO527-1，-260Yieldstrain50mm/min%ISO527-1，-24 Stressatbreak50mm/minMPaISO527-1，-250 Strainatbreak50mm/min%b.o.ISO527-1，-2>50 Izodimpactstrength23°CkJ/m²ISO180-UN Izodnotchedimpactstrength23°CkJ/m²ISO180-A35 Izodnotchedimpactstrength-30°CkJ/m²ISO180-A10ThermalpropertiesTemperatureofdeflectionunderload1.80MPa°CISO75-1，-290Temperatureofdeflectionunderload0.45MPa°CISO75-1，-2100Vicatsofteningtemperature50N50°C/h°CISO306106 Vicatsofteningtemperature50N120°C/h°CISO306108Coefficientoflinearthermalexpansion，parallel23to55°C10^-4/KISO11359-1，-20.76Coefficientoflinearthermalexpansion，transverse23to55°C10^-4/KISO11359-1，-20.8BurningbehaviorUL94(1.5mm) [ULrecognition]1.5mmClassUL94V-0BurningbehaviorUL94-5V [ULrecognition]2.2mmClassUL945VB BurningbehaviorUL94-5V [ULrecognition]3.0mmClassUL945VAElectricalproperties(23°C/50%r.h.)Relativepermittivity100Hz-IEC602503.2Relativepermittivity1MHz-IEC602503.1Dissipationfactor100Hz10^-4IEC6025040Dissipationfactor1MHz10^-4IEC6025070Volumeresistivity Ohm·mIEC600931E14Surfaceresistivity OhmIEC600931E16Electricalstrength1mmkV/mmIEC60243-135ComparativetrackingindexCTISolutionARatingIEC60112350Otherproperties(23°C)Waterabsorption(saturationvalue)Waterat23°C%ISO620.5Waterabsorption(equilibriumvalue)23°C50%r.h.%ISO620.2Density kg/m³ISO1183-11180ProcessingconditionsfortestspecimensInjectionmolding-Melttemperature °CISO294240Injectionmolding-Moldtemperature °CISO29480Injectionmolding-Injectionvelocity mm/sISO294240 Disclaimer
InformationImpactproperties
Impactproperties:N=non-break，P=partialbreak，C=completebreak