POM    507    美国杜邦公司 物性数据①原料描述部分　暂无此原料描述部分┄
　②原料技术数据性能项目试验条件[状态]测试方法测试数据数据单位基本性能密度——-ASTM D-7921.42——-物理性能吸水量24hrs浸泡+73�H(+23℃)ASTM D-5700.25%吸水量Equil.50%R.h.+73�H(+23℃)ASTM D-5700.22%吸水量浸泡均衡点+73�H(+23℃)ASTM D-5700.90%扩散因数+73�H(+23℃)10⁶HzASTM D-1500.005——-机械性能无切口冲击程度+23℃ASTM D-2561280j/m压缩应力+73�H@10% Def.ASTM D-69518.0MPsi压缩应力+23℃@10% Def.ASTM D-695124MPa负载下之变形2000psi@+122�H(14Mpa@50℃)ASTM D-6210.5%弯曲疲劳忍耐限度+73�HASTM D-6714.5MPsi弯曲疲劳忍耐限度+23℃ASTM D-67131.0MPaIZOD冲击强度-40�HASTM D-2561.2ft.lb/inIZOD冲击强度40℃ASTM D-25664.1j/mIZOD冲击强度+73�HASTM D-2561.4ft.lb/inIZOD冲击强度+23℃ASTM D-25674.7j/m拉力冲击抵抗力+73�HASTM D-1822100ft.lb/in² 拉力冲击抵抗力+23℃ASTM D-1822200kj/m² 无切口冲击程度+73�HASTM D-25624ft.lb/in断裂时之拉力伸张度-68�H(-55℃)ASTM D-63813%断裂时之拉力伸张度+73�H(+23℃)ASTM D-63840%断裂时之拉力伸张度+158�H(+70℃)ASTM D-638220%断裂时之拉力伸张度+212�H(+100℃)ASTM D-638> 260%断裂时之拉力伸张度+250�H(+122℃)ASTM D-638> 260%伸张强度-68�HASTM D-63814.7MPsi伸张强度-55℃ASTM D-638101MPa伸张强度+73�HASTM D-63810.0MPsi伸张强度+23℃ASTM D-63868.9MPa伸张强度+158�HASTM D-6386.9MPsi伸张强度+70℃ASTM D-63847.5MPa伸张强度+212�HASTM D-6385.2MPsi伸张强度+100℃ASTM D-63835.9MPa伸张强度+250�HASTM D-6383.8MPsi伸张强度+122℃ASTM D-63826.2MPa弹性系数+73�HASTM D-638450MPsi弹性系数+23℃ASTM D-6383100MPa剪力+73�HASTM D-7329.5MPsi剪力+23℃ASTM D-73265.5MPa挠曲系数-68�H在25℃下570MPsi挠曲系数-55℃在25℃下3930MPa挠曲系数+73�H在25℃下410MPsi挠曲系数+23℃在25℃下2830MPa挠曲系数+158�H在25℃下230MPsi挠曲系数+70℃在25℃下1585MPa挠曲系数+212�H在25℃下135MPsi挠曲系数+100℃在25℃下90MPsi挠曲系数+122℃在25℃下620MPa弯曲降服强度+73�HASTM D-79014.1MPsi弯曲降服强度+23℃ASTM D-79097.2MPa压缩应力+73�H@1% Def.ASTM D-6955.2MPsi压缩应力+23℃@1%Def.ASTM D-69535.9MPa洛氏硬度——-ASTM D-785M94，R120——-摩擦系数+73�H(+23℃)静态ThrustWasherTest³ 0.20——-摩擦系数+73�H(+23℃)动态ThrustWasherTest³ 0.35——-电气性能电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.绝缘强度Short Time，90 milsASTM D-149500V/mil绝缘强度Short Time，2.3mmASTM D-14919.7MV/m绝缘系数+73�H(+23℃)10²to10⁶HzASTM D-1503.7——-电阻系数+73�H(+23℃)0.2%H²OASTM D-25710¹⁵ ohm-cm热 性 能热传导系数W/mk——-0.37——-线性热膨胀系数+60 to +104℃ASTM D-69613.710^-5m/m.℃线性热膨胀系数+220 to +300�HASTM D-6968.310^-5in/in.�H线性热膨胀系数+104 to +150℃ASTM D-69614.910^-5m/m.℃热传导系数BTU-in/hr——-2.6——-熔点——-ASTM D-2133347�H熔点——-ASTM D-2133175℃线性热膨胀系数-40 to +85�HASTM D-6965.810^-5in/in.�H线性热膨胀系数-40 to +29℃ASTM D-69610.410^-5m/m.℃线性热膨胀系数+85 to +140�HASTM D-6966.810^-5in/in.�H线性热膨胀系数+29 to +60℃ASTM D-69612.210^-5m/m.℃线性热膨胀系数+140 to +220�HASTM D-6967.610^-5in/in.�H热变形温度0.5MPaASTM D-648172℃热变形温度1.8MPaASTM D-648136℃热变形温度66psiASTM D-648342�H热变形温度264psiASTM D-648277�H可燃烧性——-UL-9494HB——-