PA66美国杜邦70G13LNC010
性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTMD638/ISO527120kg/cm2(MPa)[Lb/in2]断裂伸长率 ASTMD638/ISO5273%拉伸模量 ASTMD638/ISO5275500kg/cm2(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTMD638/ISO527 %拉伸断裂伸长率(延伸率) ASTMD638/ISO527 %弯曲模量(弯曲弹性率) ASTMD790/ISO1784900kg·cm/cm(J/M)ft·lb/in弯曲强度 ASTMD790/ISO178190kg·cm/cm(J/M)ft·lb/in洛氏硬度 ASTMD785 IZOD缺口冲击强度1/4"23℃ASTMD256/ISO179 kg·cm/cm(J/M)ft·lb/in1/4"-30℃ASTMD256/ISO179 kg·cm/cm(J/M)ft·lb/in1/8"23℃ASTMD256/ISO179 kg·cm/cm(J/M)ft·lb/in1/8"-30℃ASTMD256/ISO179 kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃(缺口)ASTMD256/ISO1795kg·cm/cm(J/M)ft·lb/in-30℃(缺口)ASTMD256/ISO1794.5(-40℃)kg·cm/cm(J/M)ft·lb/in23℃(无缺口)ASTMD256/ISO17932kg·cm/cm(J/M)ft·lb/in-30℃(无缺口)ASTMD256/ISO17930kg·cm/cm(J/M)ft·lb/in物性性能比重(密度) ASTMD792/ISO11831.23 成型收缩率 ASTMD9550.7~1.2%熔融指数(流动系数)200℃/5kgASTMD1238/ISO1133 g/10min220℃/10kgASTMD1238/ISO1133 g/10min吸水率23℃/24H ASTMD570/ISO622.2%热性能热变形温度退火ASTMD648/ISO75258℃(℉)未退火ASTMD648/ISO75238℃(℉)维卡软化点 ASTMD1525/ISOR306 ℃(℉)熔点 -262℃(℉)燃烧性(率) UL94HB 线性膨胀系数 ASTMD696/ISO113590.77mm/mm.℃电气性能介电常数100HZASTMD150/IEC60250 1MHZASTMD150/IEC60250 体积电阻率 ASTMD257/IEC60093 Ω.cm表面电阻率 ASTMD257/IEC60093 Ω耐电弧性 ASTMD495/IEC60112 加工条件干燥条件 加工温度射嘴 ℃料筒前段 ℃料筒中段 ℃料筒后段 ℃熔体温度 ℃模具温度 ℃压力注塑压力 Mpa保压压力 Mpa背压 Mpa螺杆转速 rpm其他备注 颜色 特性PA66,13%玻纤增强,热稳定,注塑树脂用途