性能项目试验条件[状态]测试方法测试数据数据单位 基本性能熔体流动速率230℃/3.8kgASTM D-12382.5g/10min 物理性能比重ASTM D-7921.05g/cm3 机械性能拉伸模量3.18mmASTM D-6381480MPa 拉伸屈服强度3.18mmASTM D-63821.4MPa 拉伸断裂强度3.18mmASTM D-63825.5MPa 屈服伸长率3.18mmASTM D-6382.0% 断裂伸长率3.18mmASTM D-63845% 弯曲模量3.18mmASTM D-7901720MPa 弯曲强度3.18mmASTM D-79040.7MPa IZOD缺口冲击强度-40℃,3.18mmASTM D-25680.1J/m IZOD缺口冲击强度-29℃,3.18mmASTM D-25690.7J/m IZOD缺口冲击强度-18℃,3.18mmASTM D-25690.7J/m IZOD缺口冲击强度23℃,3.18mmASTM D-256101J/m 洛氏硬度3.18mmASTM D-78589R scale 热性能热变形温度0.45MPa,未退火ASTM D-64897.2℃ 热变形温度0.45MPa,退火ASTM D-648106℃ 热变形温度1.80MPa,未退火ASTM D-64887.2℃ 热变形温度1.80MPa,退火ASTM D-648103℃ 维卡软化温度ASTM D-1525108℃ 光学性能光泽度60℃ASTM D-523