?Glass Fiber Reinforced (Low Warpage) 
Properties Test Method Terms Units GSH2030R2 
K807 GSH2030R2 
991J 
    
GF GF 
30% 30% 
- - 
Physical properties     
Density ISO 1183 - g/cm3 1.43 1.43 
Water absorption   23degC, 50%RH % - - 
  23degC, Underwater 0.09 0.09 
Rheological properties     
Melt Mass-flow Rate ISO 1133   g/10min 15 8.8 
Melt Volume-flow Rate   cm3/10min 14 7.0 
Temperature degC 300 300 
Load kgf 1.20 1.20 
Moulding shrinkage (3.2mmt) - MD % 0.2 - 0.4 0.3 - 0.5 
TD 0.2 - 0.4 0.3 - 0.5 
Mechanical properties     
Tensile modulus ISO 527-1 
, 527-2   MPa 5100 4400 
Yield stress   - - 
Yield strain   % - - 
Nominal strain at break - - - 
Stress at 50% strain   MPa - - 
Stress at break   51 63 
Strain at break   % 1.9 2.5 
Flexural strength ISO 178 - MPa 100 100 
Flexural modulus 4600 3900 
Charpy impact strength ISO 179-1, 179-2 23 degC kJ/m2 27 30 
Charpy notched impact strength ISO 179-1, 179-2 23 degC kJ/m2 3 6 
Thermal properties     
Temperature of deflection under load ISO 75-1 
, 75-2 1.80MPa degC 134 136 
0.45MPa 140 143 
Coefficient of Linear thermal expansion ISO 11359-2 MD 1/degC - - 
TD - - 
Flammability UL94 - - HB(0.4mm) HB