中山市佳惠塑胶原料有限公司

厂家(产地)：美国杜邦牌号：100加工级别：注塑级特性级别：耐磨，热稳定性，高刚性，高强度，耐高温，抗静电用途级别：薄壁制品产品参数表：性能项目试验条件[状态]测试方法测试数据数据单位基本性能吸水量浸泡均衡点+73℉(+23℃)ASTM D5700.90%吸水量Equil.50%R.h.+73℉(+23℃)ASTM D5700.22%密度ASTM D7921.42吸水量24hrs浸泡+73℉(+23℃)ASTM D5700.25%物理性能绝缘强度Short Time，90 milsASTM D149500V/mil绝缘系数系数 +73℉(+23℃)102to106HzASTM D1503.7绝缘强度Short Time，2.3mmASTM D14919.7MV/m扩散因数+73℉(+23℃)106HzASTM D1500.005摩擦系数+73℉(+23℃)静态0.20ThrustWasherTest3摩擦系数+73℉(+23℃)动态ThrustWasherTest30.35电阻系数+73°F(+23℃)0.2%H2OASTM D2571015ohm-cm机械性能伸张强度+122℃ASTM D63826.2MPa挠曲系数+212℉在25℃下130MPsi弯曲降服强+23℃ASTM D79098.6MPa挠曲系数+122℃在25℃下620MPa伸张强度+212℉ASTM D6385.2Mpsilzod冲击强度+23℃ASTM D256123j/m洛氏硬度ASTM D785M94，R120断裂时之拉力伸张度+158℉(+70℃)ASTM D638230%伸张强度-55℃ASTM D638101MPa挠曲系数-68℉在25℃下530MPsi挠曲系数-55℃在25℃下3650MPa无切口冲击程度+23℃D256>；5300(no break)j/m挠曲系数+70℃在25℃下1550MPa挠曲系数+250℉在25℃下90MPsi压缩应力缩应力 +73°F@1%Def.ASTM D6955.2MPsi弹性系数+23℃ASTM D6383100MPa弯曲降服强+73℉ASTM D79014.3MPsilzod冲击强度40℃ASTM D25696.1j/m挠曲系数+73℉在25℃下380MPsi伸张强度+100℃ASTM D63835.9MPa压缩应力+23℃@10%Def.ASTM D695124MPa弹性系数+73℉ASTM D638450MPsi断裂时之拉力伸张度-68℉(-55℃)ASTM D63838%无切口冲击程度+73℉ASTM D256>；100(no break)ft.lb/in压缩应力+23℃@1%Def.ASTM D69535.9MPa断裂时之拉力伸张度+212℉(+100℃)ASTM D638>；260%lzod冲击强度-40℉ASTM D2561.8ft.lb/in伸张强度+23℃ASTM D-63868.9MPa负载下之变形2000psi@+122℉(14Mpa@50℃ASTM D6210.5%伸张强度-68℉ASTM D63814.7MPsi挠曲系数+23℃在25℃下2620MPa伸张强度+158℉(+70℃)ASTM D6386.9MPsi伸张强度+70℃ASTM D63847.5MPa弯曲疲劳忍耐限度+73℉ASTM D6714.7MPsi伸张强度+73℉ASTM D63810.0MPsi压缩应力+73°F@10%Def.ASTM D69518.0MPsi剪力+73℉ASTM D7329.5MPsi挠曲系数+100℃在25℃下895MPa剪力+23℃ASTM D73265.5MPa拉力冲击抵抗力+73℉D1822Long170ft.lb/in2；断裂时之拉力伸张度+73℉(+23℃)ASTM D63875%伸张强度+250℉ASTM D6383.8MPsilzod冲击强度+73℉ASTM D2562.3ft.lb/in拉力冲击抵抗+23℃D1822Long350KJ/m2弯曲疲劳忍耐限度+23℃ASTM D67132.4MPa挠曲系数+158℉在25℃下225MPsi断裂时之拉力伸张度+250℉(+122℃ASTM D638>；260%电气性能电弧抵抗力120mil(3.1mm)ASTM D495220no trackingSec.热性能熔点ASTM D2133347°F热变形温度1.8MPaASTM D648136℃线性热膨胀系数+85 to +140℉ASTM D6966.810-5in/in.℉线性热膨胀系数+140 to +220℉ASTM D6967.610-5in/in.℉线性热膨胀系数-40 to +85℉ASTM D6965.810-5in/in.℉线性热膨胀系数-40 to +29℃ASTM D69610.410-5m/m.℃热变形温度264psiASTM D648277℉线性热膨胀系数+60 to +104℃ASTM D69613.710-5m/m.℃熔点ASTM D2133175℃热传导系数0.37W/mk热变形温度0.5MpaASTM D648172℃热传导系数2.6BTU-in/hr线性热膨胀系数+220 to +300℉ASTM D6968.310-5in/in.℉热变形温度66psiASTM D648342℉线性热膨胀系数+104 to +150℃ASTM D69614.910-5m/m.℃线性热膨胀系数+29 to +60℃ASTM D69612.210-5m/m.℃其它性能可燃烧性UL9494HB产品说明：用途:用于工种制品备注:特性：均聚甲醛，高粘度，具有最坚韧的硬度，优良的热稳定性。