东莞市樟木头祥瑞塑胶原料经营部

原料技术数据性能项目试验条件[状态]测试方法测试数据数据单位基本性能密度——-ASTM D-7921.42——-物理性能吸水量24hrs浸泡+73?H(+23℃)ASTM D-5700.25%吸水量Equil.50%R.h.+73?H(+23℃)ASTM D-5700.22%吸水量浸泡均衡点+73?H(+23℃)ASTM D-5700.90%挠曲系数+70℃在25℃下1585MPa机械性能挠曲系数+158?H在25℃下230MPsi挠曲系数+212?H在25℃下90MPsi挠曲系数+122℃在25℃下620MPa弯曲降服强度+73?HASTM D-79014.1MPsi弯曲降服强度+23℃ASTM D-79097.2MPa压缩应力+73?H@1%Def.ASTM D-6955.2MPsi压缩应力+23℃@1%Def.ASTM D-69535.9MPa弹性系数+73?HASTM D-638450MPsi弹性系数+23℃ASTM D-6383100MPa剪力+73?HASTM D-7329.5MPsi剪力+23℃ASTM D-73265.5MPa挠曲系数-68?H在25℃下570MPsi挠曲系数-55℃在25℃下3930MPa挠曲系数+73?H在25℃下410MPsi挠曲系数+23℃在25℃下2830MPa断裂时之拉力伸张度-68?H(-55℃)ASTM D-63813%断裂时之拉力伸张度+73?H(+23℃)ASTM D-63840%断裂时之拉力伸张度+158?H(+70℃)ASTM D-638220%断裂时之拉力伸张度+212?H(+100℃)ASTM D-638> 260%断裂时之拉力伸张度+250?H(+122℃)ASTM D-638> 260%断裂时之拉力伸张度+250?H(+122℃)ASTM D-638> 260%伸张强度-68?HASTM D-63814.7MPsi伸张强度-55℃ASTM D-638101MPa伸张强度+73?HASTM D-63810.0MPsi伸张强度+158?HASTM D-6386.9MPsi伸张强度+70℃ASTM D-63847.5MPa伸张强度+212?HASTM D-6385.2MPsi伸张强度+100℃ASTM D-63835.9MPa伸张强度+250?HASTM D-6383.8MPsi伸张强度+122℃ASTM D-63826.2MPa压缩应力+73?H@10%Def.ASTM D-69518.0MPsi压缩应力+23℃@10%Def.ASTM D-695124MPa负载下之变形2000psi@+122?H(14MPa@50℃)ASTM D-6210.5%弯曲疲劳忍耐限度+73?HASTM D-6714.5MPsi弯曲疲劳忍耐限度+23℃ASTM D-67131.0MPaIZOD冲击强度-40?HASDM D-2561.2ft.lb/inIZOD冲击强度40℃ASDM D-25664.1j/mIZOD冲击强度+73?HASDM D-2561.4ft.lb/inIZOD冲击强度+23℃ASTM D-25674.7j/m拉力冲击抵抗力+73?HASTM D-1822100ft.lb/in² 拉力冲击抵抗力+23℃ASTM D-1822200kj/m² 无切口冲击程度+73?HASDM D-25624ft.lb/in无切口冲击程度+23℃ASDM D-2561280j/m熔点——-ASTM D-2133175℃扩散因数+73?H(+23℃)10⁶HzASTM D-1500.005——-洛氏硬度——-ASTM D-785M94，R120——-摩擦系数+73?H(+23℃)静态ThrustWasherTest³ 0.20——-摩擦系数+73?H(+23℃)动态ThrustWasherTest³ 0.35——-电气性能电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.绝缘强度Short Time，90 milsASTM D-149500V/mil绝缘强度Short Time，2.3mmASTM D-14919.7MV/m绝缘系数+73?H(+23℃)10²to10⁶HzASTM D-1503.7——-电阻系数73?H(+23℃)0.2%H₂0ASDM D-25710¹⁵ ohm-cm伸张强度+23℃ASTM D-63868.9MPa热 性 能热传导系数——————0.37W/mk线性热膨胀系数+60 to +104℃ASTM D-69613.710^-5m/m.℃线性热膨胀系数+220 to +300?HASTM D-6968.310^-5in/in.°F线性热膨胀系数+104 to +150℃ASTM D-69614.910^-5m/m.℃热传导系数——————2.6BTU-in/hr线性热膨胀系数-40 to +85?HASTM D-6965.810^-5in/in.?H熔点——-ASTM D-2133347?H线性热膨胀系数-40 to +29℃ASTM D-69610.410^-5m/m.℃线性热膨胀系数+85 to +140?HASTM D-6966.810^-5in/in.?H线性热膨胀系数+29 to +60℃ASTM D-69612.210^-5m/m.℃线性热膨胀系数+140 to +220?HASTM D-6967.610^-5in/in.°F热变形温度0.5MPaASTM D-648172℃热变形温度1.8MPaASTM D-648136℃热变形温度66psiASTM D-648342?H热变形温度264psiASTM D-648277?H可燃烧性——-UL-9494HB——-