乐泰3220 LOCTITE 3220 is designed for use in heat sensitivedevices.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Casson Viscosity @ 25 °C, mPa?s (cP):
Haake PK 100, M10/PK 1 2° Cone
Yield Point @ 25°C, MPa
Specific Gravity
Pot Life @ 25oC, days
Flash Point - See MSDS
TYPICAL CURING PERFORMANCE
Cure Schedule
5 to 10 minutes @ 80°C
With all curing systems, the time required for cure depends onthe rate
of heating. Cure rate depends on the mass of material to beheated
and intimate contact with the heat source. Use suggestedcure
conditions as general guidelines. Other cure conditions mayyield
satisfactory results.
 
乐泰3513是一种单组份环氧的可维修的底部填充树脂，适用于CSP（FBGA）以及BGA.加热后可快速固化。抗机械应力出色。低粘度树脂可充分的填充CSP和BGA的底部。
汉高LOCTITE3513
  固化后材料的性能：
  固化前的材料特性：（100°C固化60分钟）
  典型值
  化学类型环氧树脂
  外观淡黄色液体
  比重＠25°C 1.15
  粘度＠25°C，mPa?s
  HAAKE粘度计，PK1，2°
  Constant shear rate＠36 1／s 4，000
  使用寿命＠23°C，48小时
  典型值
  剪切强度，ASTM D1002，N／mm2
  喷沙低碳钢 16
  环氧玻璃 10
  典型的抗环境能力：
  试验方法 ASTM D1002
  基材环氧玻璃
  固化工艺100°C，60分钟
  固化条件的推荐：
  150°C维持10分钟
  120°C维持15分钟
  热强度：100°C维持30分钟